Mineral filled grade polypropylene P212AT
| Detailed product specification | |||||||||
| Name | Mineral filled grade polypropylene | Model | P212AT | Appearance color | Natural Color | ||||
| processing technic | Injection molding |
||||||||
| performance feature | High strength, high surface gloss, high hardness, high elongation at break, easy color matching, easy molding. |
||||||||
| environmental protection class | ROHS、SGS | ||||||||
| Fill/enhance | Mineral filling grade |
||||||||
| application | Household appliances shell, sanitary ware, auto parts, auto parts, kitchen accessories, etc. |
||||||||
| processing conditions | injection moulding |
||||||||
| Performance technical parameters | |||||||||
| basic performance |
Test item | Test condition | test method | test data | data unit | ||||
| density |
ASTM D-792 | 1.021 | g/cm3 | ||||||
| Melt flow rate | 230°C/2.16 kg | ASTM D-1238 | 8 | g/10 min | |||||
| shrinking rate | Internal Method | 1.3-1.5 | % | ||||||
| Rockwell hardness | R measurement | ASTM D-785 | 105 | R | |||||
| Mechanical performance |
tensile strength | ASTM D-638 | 28 | MPa | |||||
| bending strength | 23°C | ASTM D-638 | 32 | MPa | |||||
| elongation at break | ASTM D-638 | 40 | % | ||||||
| bending modulus | 23°C | ASTM D-790A | 1450 | MPa | |||||
| Notch impact strength of suspension beam |
23°C | ASTM D-256 | 8.5 | KJ/㎡ | |||||
| thermal performance |
distortion temperature | 1.8 MPa,unannealed | ASTM D-648 | 115 | ℃ | ||||
| Softening temperature of microcard |
ISO306 | 152 | ℃ | ||||||
| electrical performance |
CTI | SOLUTION A | IEC60112 | / | V | ||||
| volume resistance | 23°C 50%RH | ASTM D-257 | / | OHM-CM | |||||
| flammability |
UL Rating | 1.60mm | UL 94 | HB | |||||
| 3.20mm | UL 94 | HB | |||||||
| Flammability Normal thickness 1.60mm (1.50mm UL) | ISO1210 UL94 | HB | |||||||
| Note: The above processing data bit reference values, please adjust according to the actual production and processing conditions. | |||||||||