Mineral filled grade polypropylene P212KT

Mineral filled grade polypropylene P212KT
 

Detailed product specification
Name		Mineral filled grade polypropylene	Model		P212KT		Appearance color		Natural Color
processing technic		Injection molding
performance feature		High strength, high surface gloss, high hardness, high elongation at break, easy color matching, easy molding.
environmental protection class		ROHS、SGS
Fill/enhance		Mineral filling grade
application		Household appliances shell, sanitary ware, auto parts, auto parts, kitchen accessories, etc.
processing conditions		injection moulding
Performance technical parameters
basic performance	Test item			Test condition		test method		test data		data unit
	density					ASTM D-792		1.0		g/cm3
	Melt flow rate			230°C/2.16 kg		ASTM D-1238		8		g/10 min
	shrinking rate					Internal Method		1.3-1.5		%
	Rockwell hardness			R measurement		ASTM D-785		95		R
Mechanical performance	tensile strength					ASTM D-638		24		MPa
	bending strength			23°C		ASTM D-638		27		MPa
	elongation at break					ASTM D-638		655		%
	bending modulus			23°C		ASTM D-790A		1203		MPa
	Notch impact strength of suspension beam			23°C		ASTM D-256		26		KJ/㎡
thermal performance	distortion temperature			1.8 MPa,unannealed		ASTM D-648		110		℃
	Softening temperature of microcard					ISO306		150		℃
electrical performance	CTI			SOLUTION A		IEC60112		/		V
	volume resistance			23°C  50%RH		ASTM D-257		/		Ohm - cm
flammability	UL Rating			1.60mm		UL 94		HB
				3.20mm		UL 94		HB
	Flammability Normal thickness 1.60mm (1.50mm UL)					ISO1210 UL94		HB		HB
Note: The above processing data bit reference values, please adjust according to the actual production and processing conditions.