PA66 Mineral filled
Product Description:
Modified PA 66 for injection moulding with the contenct of 30% microground, chemically modified talc. Increased strength, rigidity and thermal application up to 200°C depending on the talc content. Decreased shrinkage. Improved impact strenght. Delivered in the full RAL colour scale.
Application
Automotive Applications, Gears, Power/Other Tools
Minimum order quantity
1 | |
| Brand Name: | HENGA | ||
| Color: | NATURE | ||
| Model Number: | HG-PA66-MF001 | ||
| Certificates: | REACH, ROHS, TS16949 | ||
| Filler / Reinforcement | Talc, 30% Filler by Weight | ||
| Features | Heat Stabilized | ||
| Usage: | Automotive Applications,Gears,Power/Other Tools | ||
| Delivery time: | 3-5days | ||
| Physical | Nominal Value | Unit | Test Method |
| Density | 1.34 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (270°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 0.8 | % | |
| Flow | 0.5 | % | |
| Water Content | 0.1 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus | 5400 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 75 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.5 | % | ISO 527-2 |
| Flexural Modulus | 3800 | MPa | ISO 178 |
| Flexural Stress | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 3.5 | kJ/m² | |
| 23°C | 4 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 50 | kJ/m² | |
| 23°C | 70 | kJ/m² | |
| Thermal | Nominal Value | Unit | Test Method |
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 65 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 185 | °C | ISO 306/B |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 60 to 90 | °C | |
| Injection Pressure | 80.0 to 120 | MPa |
PA66 Mineral filled
.jpg)