Detailed product specification | ||||||||||
Name | Glass fiber reinforced polypropylene |
Model | P110GHQ | Appearance color |
Natural | |||||
processing technic |
Injection molding | |||||||||
performance feature |
Ultra high hardness, superior impact strength, low shrinkage, good dimensional stability, easy color matching and molding. | |||||||||
environmentalprotection class |
ROHS、SGS | |||||||||
Fill/enhance | glass fibre reinforcement | |||||||||
application | Electrical components, bracket, auto parts, water pump parts, screw blades, furniture accessories, etc. | |||||||||
processing conditions |
injection moulding | |||||||||
Performance technical parameters | ||||||||||
basic performance | Test item | Test condition | test method | test data | data unit | |||||
density |
ASTM D-792 | 0.986 | g/cm3 | |||||||
Melt flow rate | 230°C/2.16 kg | ASTM D-1238 | 12 | g/10 min | ||||||
shrinking rate | Internal Method | 1.3-1.5 | % | |||||||
Rockwell hardness | R measurement | ASTM D-785 | 110 | R | ||||||
Mechanical performance | tensile strength | ASTM D-638 | 53 | MPa | ||||||
bending strength | 23°C | ASTM D-638 | 55 | MPa | ||||||
elongation at break | ASTM D-638 | 6 | % | |||||||
bending modulus | 23°C | ASTM D-790A | 2200 | MPa | ||||||
Notch impact strength of suspension beam |
23°C | ASTM D-256 | 8 | KJ/㎡ | ||||||
thermal performance | distortion temperature | 1.8 MPa,unannealed | ASTM D-648 | 115 | ℃ | |||||
Softening temperature of microcard |
ISO306 | 150 | ℃ | |||||||
electrical performance | CTI | SOLUTION A | IEC60112 | / | V | |||||
volume resistance | 23°C 50%RH | ASTM D-257 | / | OHM-CM | ||||||
flame ability | UL Rating | 1.60mm | UL 94 | HB | ||||||
3.20mm | UL 94 | HB | ||||||||
Flammability Normal thickness 1.60mm (1.50mm UL) | ISO1210 UL94 | HB | ||||||||