| Detailed product specification | ||||||||||
| Name | Glass fiber reinforced polypropylene |
Model | P140GHQ | Appearance color |
Natural | |||||
Processing technic |
Injection molding | |||||||||
| Performance feature | Ultra high hardness, superior impact strength, low shrinkage, good dimensional stability, easy color matching and molding. | |||||||||
| Environmental protection class | ROHS、REACH | |||||||||
| Fill/enhance | Glass fibre reinforcement | |||||||||
| Application | Electrical components, bracket, auto parts, water pump parts, screw blades, furniture accessories, etc. | |||||||||
| Production way | Injection/molding | |||||||||
| Performance technical parameters | ||||||||||
| href="javascript:;" Basic performance | Test item | Test condition | test method | test data | data unit | |||||
| density |
ASTM D-792 | 1.126 | g/cm3 | |||||||
| Melt flow rate | 230°C/2.16 kg | ASTM D-1238 | 7 | g/10 min | ||||||
| shrinking rate | Internal Method | 0.8-1.0 | % | |||||||
| Rockwell hardness | R measurement | ASTM D-785 | 125 | R | ||||||
| Mechanical performance | Tensile strength | ASTM D-638 | 64 | MPa | ||||||
| Bending strength | 23°C | ASTM D-638 | 95 | MPa | ||||||
| Elongation at break | ASTM D-638 | 47 | % | |||||||
| Bending modulus | 23°C | ASTM D-790A | 5390 | MPa | ||||||
| Notch impact strength of suspension beam |
23°C | ASTM D-256 | 10 | KJ/㎡ | ||||||
| thermal performance | Distortion temperature | 1.8MPa,unannealed | ASTM D-648 | 130 | ℃ | |||||
| Softening temperature of microcard |
ISO306 | 160 | ℃ | |||||||
| electrical performance | CTI | SOLUTION A | IEC60112 | / | V | |||||
| volume resistance | 23°C 50%RH | ASTM D-257 | / | OHM-CM | ||||||
| flammability | UL Rating | 1.60mm | UL 94 | HB | ||||||
| 3.20mm | UL 94 | HB | ||||||||
| Flammability Normal thickness 1.60mm (1.50mm UL) | ISO1210 UL94 | HB | ||||||||
| Remarks: The above processing data bit reference values, please adjust according to the actual production and processing conditions. | ||||||||||
Toughend polypropylene P140GHQ