high strength fr gf reinforced pc granules/ pc pellets gf30 fr for vehicle accessories
flame retardant; high viscosity; only opaque colors available; V-0/1.5mm (UL 94); V-0/3.0mm (UL 94); 5VA/3.0mm (UL 94); 'softening temperature (VST/B 120)=185°C; injection molding - melt temperature 330 - 340°C
Minimum order quantity
1 | |
| Brand Name: | HENGA | ||
| Color: | NATURE | ||
| Model Number: | HG-PC-FR001 | ||
| Certificates: | REACH, ROHS, TS16949 | ||
| Usage: | Connectors Electrical/Electronic Applications Housings Construction Applications Household Goods Plugs |
||
| Delivery time: | 3-5days | ||
| Physical | Nominal Value | Unit | Test Method |
| Density (23°C) | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (330°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (330°C/2.16 kg) | 12 | cm³/10min | ISO 1133 |
| Molding Shrinkage 3 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.85 | % | |
| Flow : 2.00 mm | 0.85 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.3 | % | |
| Equilibrium, 23°C, 50% RH | 0.12 | % | |
| Hardness | Nominal Value | Unit | Test Method |
| Ball Indentation Hardness | 121 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 72 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 6.8 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 50 | % | ISO 527-2/50 |
| Flexural Modulus 4 (23°C) | 2400 | MPa | ISO 178 |
| Flexural Stress 4 (23°C) | 108 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Thermal | Nominal Value | Unit | Test Method |
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 174 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 159 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 185 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 6.50E-05 | cm/cm/°C | |
| Transverse : 23 to 55°C | 6.50E-05 | cm/cm/°C | |
| Electrical | Nominal Value | Unit | Test Method |
| Surface Resistivity | 1.00E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.00E+16 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 2.9 | ||
| 23°C, 1 MHz | 2.8 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 1.00E-03 | ||
| 23°C, 1 MHz | 9.00E-03 | ||
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 225 | V | |
| Solution B | 100 | V | |
| Flammability | Nominal Value | Unit | Test Method |
| Flame Rating (1.5 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.0 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index 5 | 35 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Test Method | |
| Electrolytical Corrosion (23°C) | A1 | IEC 60426 | |
| Injection | Nominal Value | Unit | |
| Drying Temperature - Dry Air Dryer | 130 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 315 to 325 | °C | |
| Middle Temperature | 320 to 330 | °C | |
| Front Temperature | 325 to 335 | °C | |
| Nozzle Temperature | 315 to 340 | °C | |
| Processing (Melt) Temp | 320 to 340 | °C | |
| Mold Temperature | 100 to 140 | °C | |
| Back Pressure | 10.0 to 20.0 | MPa | |
| Vent Depth | 0.025 to 0.050 | mm | |
| Injection Notes | |||
| Hold Pressure (% of Injection Pressure): 50 - 75% | |||
| Peripheral Screw Speed: 0.05 - 0.2 m/s | |||
| Standard Melt Temperature: 335°C | |||